ALLMAX®
I
19 - 21 % chromium, carbon content ~ 2.4 - 2.9 %
ALLMAX®
II
11
- 13 % chromium, carbon content ~ 2.4 - 3.3 %
CR3
23
- 25% chromium, carbon content ~ 2.4 - 2.8 %
 |
Multi-Stage Hardening and Tempering ~ Hardness ~ 60 - 65 HRc |
|
Microstructure: up to 40% chromium carbides (M7 C3 Type) embedded in a high carbon martensitic matrix |
|
Remaining austenite content below 4% |
Christian
Pfeiffer Mezzomerico
www.christianpfeiffer.it
(our
foundry in Italy)
ALLMAX®
CAST GRINDING MEDIA
Forged
media also available.
|
HIGHEST WEAR RESISTANCE
SHAPE STABILITY THROUGHOUT SERVICE LIFE
UNIFORM HARDNESS SURFACE TO CENTER
|
ALLMAX®
I
|
ALLMAX®
II
|
||
|
Balls:
|
Ø
100 - 18 mm Ø 4 in - 3/4 in |
Balls:
|
Ø
100 - 15 mm Ø 4 in - 1/2 in |
|
Cylpebs:
|
35x35
mm 30x30 mm 25x25 mm 22x22 mm 19x19 mm |
Cylpebs:
|
35x35
mm 30x30 mm 25x25 mm 22x22 mm 19x19 mm 16x16 mm 12x12 mm |